| TECHNICAL
CHARACTERISTICS |
|
|
ECOBIOCOMPATIBLE PANELS
ACCORDING TO ANAB
- IBO - IBN |
| Characteristics |
M.U. |
CELENIT
N
CELENIT
NB
|
CELENIT
A
CELENIT
AB
|
CELENIT
R
CELENIT
RB
|
CELENIT S
|
| 15 |
20 |
25 |
30 |
35 |
40 |
50 |
75 |
15 |
25 |
35 |
50 |
50 |
75 |
25 |
35 |
50 |
| Medium
weight |
kg/m2 |
8 |
10 |
11,5 |
13 |
14 |
16 |
18 |
26 |
9 |
13 |
16 |
21 |
18 |
26 |
13 |
16 |
21 |
| Thermal
resistance at 10 °C |
m2K/W |
0,2 |
0,27 |
0,35 |
0,43 |
0,53 |
0,61 |
0,81 |
1,22 |
0,20 |
0,35 |
0,53 |
0,81 |
0,81 |
1,22 |
0,35 |
0,53 |
0,81 |
| Average
resistance to flexion (*) |
N/mm2 |
3,51 |
3,33 |
3,15 |
2,55 |
1,94 |
1,82 |
1,71 |
1,16 |
3,51 |
3,15 |
1,94 |
1,71 |
2,5 |
1,5 |
3,15 |
1,94 |
1,71 |
| Average
resistance to compression by pressing 10% |
N/mm2 |
0,2 |
0,2 |
0,2 |
0,2 |
0,2 |
0,15 |
0,15 |
0,15 |
0,2 |
0,2 |
0,2 |
0,15 |
0,28 |
0,27 |
0,2 |
0,2 |
0,15 |
| Reaction
to fire |
class |
1 (B1) |
1
(B1) |
1
(B1) |
1
(B1) |
| Resistance
to vapour |
μ |
4-6
|
4-6 |
4-6 |
4-6 |
| Resistance
to water and frost |
20
cycles frost/defrost |
no alteration |
no
alteration |
no
alteration |
no
alteration |
| Temperature
limit for use |
°C |
200
|
200 |
200 |
200 |
| Capacity
of absorption of room humidity |
lt/m2 |
2-3,5
|
2-3,5 |
2-3,5 |
2-3,5 |
| Specific
heat |
kJ/kgK |
2,1
|
2,1 |
2,1 |
2,1 |
| Capacity
for thermal accumulation |
kJ/m3K |
1119-726
|
1260-882 |
756-726 |
1092-882 |
| Linear
dilatation thermal coefficient |
mm/mK |
0,01
|
0,01 |
0,01 |
0,01 |
| Resistance
to traction perpendicular to the face |
N/mm2 |
0,05
|
0,05 |
0,05 |
0,05 |
| Resistance
to cutting |
N/mm2 |
0,28
|
0,28 |
0,28 |
0,28 |
| Adhesion
to concrete |
N/mm2 |
0,05
|
0,05 |
0,05 |
0,05 |
| Resistance
to mould and fungus attack |
|
Inhibition |
Inhibition |
Inhibition |
Inhibition |
(*) For the applications the minimum values
for DIN 1101 norms apply.
| Characteristics |
M.U. |
CELENIT
P2
CELENIT
P2B
|
CELENIT P3
|
CELENIT L3
|
| 30 |
35 |
40 |
50 |
75 |
25 |
35 |
50 |
75 |
35 |
50 |
75 |
| Medium
weight |
kg/m2 |
6,5 |
6,5 |
6,7 |
7,0 |
7,2 |
8,0 |
8,2 |
8,5 |
9,0 |
11 |
12 |
16 |
| Thermal
resistance at 10 °C |
m2K/W |
0,58 |
0,71 |
0,83 |
1,09 |
1,73 |
0,45 |
0,71 |
1,09 |
1,73 |
0,70 |
1,06 |
1,68 |
| Average
resistance to flexion |
N/mm2 |
- |
1,0 |
0,7 |
0,5 |
0,4 |
0,7 |
0,5 |
0,4 |
| Average
resistance to compression by pressing 10% |
N/mm2 |
0,05 |
0,05 |
0,05 |
| Reaction
to fire |
class |
1
(B1) |
1
(B1) |
1
(B1) |
| Resistance
to vapour |
μ |
50 |
50 |
4-5 |
| Temperature
limit for use |
°C |
- |
- |
200 |
| Resistance
to traction perpendicular to the face |
N/mm2 |
0,03 |
0,03 |
0,024 |
| Adhesion
to concrete |
N/mm2 |
0,05 |
0,05 |
0,05 |
| Resistance
to mould and fungus attack |
|
Inhibition |
Inhibition |
Inhibition |
|